JQ.MH00Cr21Ni10 stainless steel submerged-arc welding wire

1. The temperature between welds is recommended to be controlled at about 150°C. When multi-pass multi-layer welding of small and medium-sized specifications, pay attention to controlling the welding line energy. 2. The rust layer, moisture, oil, dust, etc. of the welding part must be cleaned up. 3. The flux must be baked at 300-350℃ for 2h before use.

Products Details

Widely used in petrochemical and other industries, such as welding of 022Cr18Ni9 (SUS 304L) and other materials.

Model

Welding wire chemical composition(Wt%)

C

Mn

Si

Cr

Ni

P

S

Cu

other

JQ.MH00Cr21Ni10

0.027

1.75

0.57

20.27

9.56

0.023

0.010

-

-

Compliant (equivalent) standard model

An example of physical properties of deposited metal (with SJ601)

GB

AWS

Tensile StrengthMPa

Elongation%

F308L-H00Cr21Ni10

ER308L

568

35.5

Diameter(mm)

¢2.5

¢3.2

¢4.0

¢5.0

Welding current(A)

400-500

450-550

500-600

550-650

Wire diameter

¢2.5

¢3.2

¢4.0

¢5.0

Package weight

25/50/100/200/250/300/350Kg/piece

1. The temperature between welds is recommended to be controlled at about 150°C. When multi-pass multi-layer welding of small and medium-sized specifications, pay attention to controlling the welding line energy. 2. The rust layer, moisture, oil, dust, etc. of the welding part must be cleaned up. 3. The flux must be baked at 300-350℃ for 2h before use. The above suggestions are for reference only, and the actual situation shall prevail in the specific operation. If necessary, process qualification should be carried out before determining the welding plan.