H1Cr24Ni13 Stainless Steel Argon-arc Welding Wire

1. Protective gas: pure Ar; flow rate: 9-14L/min when the current is 100-200A, 14-18L/min when the current is 200-300A. 2. Tungsten electrode extension length: 3-5mm; arc length: 1-3mm. 3. The wind speed is limited to ≤1.0m/s; it is recommended to pass argon protection on the back of the welding area. 4. In welding, the magnitude of the welding line energy directly affects the mechanical properties and crack resistance of the weld metal, and more attention should be paid to it. 5. Make sure to remove the rust layer, moisture, oil, dust, etc. on the welding part.

Products Details

It is often used for welding the same type of stainless steel, stainless steel lining, dissimilar steel (06Cr19Ni10 and low carbon steel) and high Cr, high Mn steel, etc.

Model

Welding wire chemical compositionWt%)

 

C

Mn

Si

Cr

Ni

Mo

P

S

Cu

H1Cr24Ni13

0.06

2.05

0.34

23.83

13.26

0.23

0.020

0.011

0.06

Compliant (equivalent) standard model

An example of physical properties of deposited metal (with SJ601)

GB

AWS

Tensile StrengthMPa

Elongation%

S309

ER309

604

40.5

Diameter(mm)

¢1.6

¢2.0

¢2.5

¢3.2

Welding current(A)

50-100

100-200

200-300

300-400

Wire diameter

¢1.6

¢2.0

¢2.5

Package weight

5Kg/plastic box,20Kg/carton(Contains 4 small plastic boxes)

1. Protective gas: pure Ar; flow rate: 9-14L/min when the current is 100-200A, 14-18L/min when the current is 200-300A. 2. Tungsten electrode extension length: 3-5mm; arc length: 1-3mm. 3. The wind speed is limited to ≤1.0m/s; it is recommended to pass argon protection on the back of the welding area. 4. In welding, the magnitude of the welding line energy directly affects the mechanical properties and crack resistance of the weld metal, and more attention should be paid to it. 5. Make sure to remove the rust layer, moisture, oil, dust, etc. on the welding part. The above suggestions are for reference only, and the actual situation shall prevail in the specific operation. If necessary, process qualification should be carried out before determining the welding plan.